We use cookies to ensure that we give you the best experience on our website. If you click 'Accept all cookies' we'll assume that you are happy to receive all cookies and you won't see this message again. If you click 'Reject all non-essential cookies' only necessary cookies providing core functionality such as security, network management, and accessibility will be enabled. Click 'Find out more' for information on how to change your cookie settings.

Electrospun filaments are leading to a new generation of medical yarns that have the ability to enhance tissue healing through their biophysical cues. We have recently developed a technology to fabricate continuous electrospun filaments by depositing the submicron fibres onto a thin wire. Here we investigate the influence of pyridine on the fibre deposition. We have added pyridine to polydioxanone solutions at concentrations ranging from 0 to 100 ppm, increasing the conductivity of the solutions almost linearly from 0.04 uS/cm to 7 uS/cm. Following electrospinning, this led to deposition length increasing from 1 cm to 14 cm. The samples containing pyridine easily underwent cold drawing. The strength of drawn filaments increased from 0.8 N to 1.5 N and this corresponded to a decrease in fibre diameter, with values dropping from 2.7 μm to 1 μm. Overall, these findings are useful to increase the reliability of the manufacturing process of continuous electrospun filaments and to vary their biophysical properties required for their application as medical yarns such as surgical sutures.

Original publication




Journal article


Plos one

Publication Date





Biophysical Phenomena, Electric Conductivity, Humans, Nanofibers, Polydioxanone, Polyesters, Pyridines, Solutions, Sutures, Tensile Strength, Tissue Scaffolds